Gyda datblygiad gwyddoniaeth a thechnoleg, bwrdd cylched printiedigwedi dod yn elfen electronig anhepgor, y bwrdd cylched printiedig wedi cael ei ail-enwi fel is-haen anorganig substrate.Traditional electronig ar gyfer Al2O3, a SIC, BeO ac ADY swbstrad, deunyddiau hyn yn y dargludedd thermol, plygu cryfder a cyfernod ehangu thermol mae perfformiad da, yn awr a ddefnyddir yn eang yn y diwydiannau astudio MCM substrate.The o'r deunydd PCB Ceramig yn Al2O3 micron ac CaZrO3 fel y prif deunydd crai, gan ddefnyddio ffwrnais gwrthiant silicon carbid sintro, ac archwilio'r dwysedd cymharol, cyson dielectric ac eiddo colled deuelectrig.
Dadansoddiad dwysedd 1.Relative 
The influence of the relative density of alumina ceramic integrated circuit substrate with different micron Al2O3 and nano CaZrO3 powder was added.By a figure known as the temperature increases, the relative density with the increase of substrate material, temperature of 1100 ℃ maximum.When micron Al2O3 content is 60 wt %, the adding amount of nano ZrO2 is 10 wt %, the relative density of alumina ceramic pcb substrate integrated material relative to other formula is the largest, the sample is relatively dense, is beneficial to integration of alumina ceramics substrate material mechanics performance improvement.
Dadansoddiad cyson 2.Dielectric 
The above is the dielectric constant of the PCB Ceramig material with the curve of sintering temperature.It can be seen that as the temperature rises, its dielectric constant increases.When the temperature reached 1100 ℃, the dielectric constant peak.When the addition of micron Al2O3 was changed from 50 wt% to 65 wt %, and the addition of nano-cazro3 was changed from 20 wt% to 5 wt %, the dielectric constant of the alumina integrated electric subgrade plate was first increased and then decreased.When the content of micron Al2O3 was 60 wt% and the content of nano CaZrO3 was 10 wt %, the sample performance was the best.This is because the factors that influence the dielectric constant are multifaceted, as long as the chemical composition of the formulation is involved, the more the alkali metal ion oxide content is, the greater the permittivity is.In addition, the thermal exercise of the ions and dipoles in the process of rising temperature increases, resulting in an increase in the permittivity.
Dadansoddiad colled 3.Dielectric 
The above is the dielectric loss of the ceramic pcb cesubstrate material with the sintering temperature curve.As the temperature increases, the dielectric loss gradually decreases.When the micron Al2O3 in 50 wt % 65 wt % change between nano CaZrO3 between 20 wt % to 5 wt % change, dielectric loss reduced after increased first, when the micron Al2O3 content is 60 wt %, nano CaZrO3 amount to 10 wt %, and when the sintering temperature is 1100 ℃, the dielectric loss value of the minimum sample after sintering.
The dielectric loss of the ceramic pcb material is caused by the internal electron, ion drain and space charge polarization, and the smaller the volume resistivity of the material, the larger the dielectric loss.Of the existence of samples CaZrO3 Ca (superscript 2 +) ions of other low price and tetravalent Zr ions produce depressive effect, make the dielectric loss of samples increased, the Na2O and the existence of K2O, makes the ion K and Na ions as a result of the action of the double effect of alkali, make the network combined with close, so the sample dielectric loss less.