Uban sa pagpalambo sa siyensiya ug teknolohiya, naimprinta nga circuit boardnahimong usa ka importante nga electronic nga bahin, ang pinatik nga sirkito nga board nga ngalan ingon nga electronic substrate.Traditional organikong substrate alang sa Al2O3, ug musika, BeO ug AlN substrate, kini nga mga nga mga materyal sa sa sa kainit conductivity, bending kusog ug sa kainit nga pagpalapad coefficient adunay usa ka maayo nga performance, ang karon kaylap nga gigamit sa mga industriya sa MCM substrate.The pagtuon sa mga seramik PCB materyal nga mao ang micron Al2O3 ug CaZrO3 ingon nga ang mga nag-unang hilaw nga materyal nga, sa paggamit sa pagsukol hudno sintering silicon carbide, ug usisa sa mga paryente Densidad, dielectric kanunay ug dielectric pagkawala kabtangan.
1.Relative Densidad pagtuki 
The influence of the relative density of alumina ceramic integrated circuit substrate with different micron Al2O3 and nano CaZrO3 powder was added.By a figure known as the temperature increases, the relative density with the increase of substrate material, temperature of 1100 ℃ maximum.When micron Al2O3 content is 60 wt %, the adding amount of nano ZrO2 is 10 wt %, the relative density of alumina ceramic pcb substrate integrated material relative to other formula is the largest, the sample is relatively dense, is beneficial to integration of alumina ceramics substrate material mechanics performance improvement.
2.Dielectric kanunay nga pagtuki 
The above is the dielectric constant of the seramik PCB material with the curve of sintering temperature.It can be seen that as the temperature rises, its dielectric constant increases.When the temperature reached 1100 ℃, the dielectric constant peak.When the addition of micron Al2O3 was changed from 50 wt% to 65 wt %, and the addition of nano-cazro3 was changed from 20 wt% to 5 wt %, the dielectric constant of the alumina integrated electric subgrade plate was first increased and then decreased.When the content of micron Al2O3 was 60 wt% and the content of nano CaZrO3 was 10 wt %, the sample performance was the best.This is because the factors that influence the dielectric constant are multifaceted, as long as the chemical composition of the formulation is involved, the more the alkali metal ion oxide content is, the greater the permittivity is.In addition, the thermal exercise of the ions and dipoles in the process of rising temperature increases, resulting in an increase in the permittivity.
3.Dielectric kapildihan pagtuki 
The above is the dielectric loss of the ceramic pcb cesubstrate material with the sintering temperature curve.As the temperature increases, the dielectric loss gradually decreases.When the micron Al2O3 in 50 wt % 65 wt % change between nano CaZrO3 between 20 wt % to 5 wt % change, dielectric loss reduced after increased first, when the micron Al2O3 content is 60 wt %, nano CaZrO3 amount to 10 wt %, and when the sintering temperature is 1100 ℃, the dielectric loss value of the minimum sample after sintering.
The dielectric loss of the ceramic pcb material is caused by the internal electron, ion drain and space charge polarization, and the smaller the volume resistivity of the material, the larger the dielectric loss.Of the existence of samples CaZrO3 Ca (superscript 2 +) ions of other low price and tetravalent Zr ions produce depressive effect, make the dielectric loss of samples increased, the Na2O and the existence of K2O, makes the ion K and Na ions as a result of the action of the double effect of alkali, make the network combined with close, so the sample dielectric loss less.